Contatto

Siamo a vostra disposizione da lunedì a venerdì dalle ore 8:00 alle ore 17:00. In questo link troverete le persone di contatto per la vostra regione.

Sede di Wolfurt
+43 5574 6706-0

Il vostro referente

SHOP

Carrello acquisti {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Articoli Cambia carrello acquisti

Nota

Foto

Articoli

Pz.

Prezzo singolo

Prezzo unitario

Prezzo unitario incluso lo sconto

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

La preghiamo di registrarvi per vedere i vostri prezzi e per poter procedere con l’acquisto.

La nostra vasta gamma permette di trovare il materiale idoneo per quasi tutte le applicazioni.

1.2738 Tool steel

Designation

DIN:	40 CrMnNiMo 8-6-4
AFNOR:	40 CMND 8
UNI:	-
AISI:	≈ P20 + Ni

Chemical composition:

C	0.40
Mn	1.50
Cr	1.90
Mo	0.20
Ni	1.10
Si	0.30

Strength:

280 - 325 HB
(≈ 950 - 1100 N/mm²)

Thermal conductivity at 100 °C:

33.5 W/m K

Character:

low-sulphur tool steel, supplied in pre-toughened condition; due to its nickel content, it features uniform strength even with maximum plate dimensions

Application:

large cavity plates with deep cavities for items such as bumpers or dashboards, moulding frames

Treatment by

highly suitable:
Polishing, EDM, nitriding, etching

suitable:
Hard chrome

Heat treatment:

already pre-toughened; usually no heat treatment required

Soft annealing:
710 to 740 °C for about 2 to 5 hours; slow controlled cooling of 10 to 20 °C per hour to about 600 °C further cooling in air, max. 220 HB

Hardening:
840 to 870 °C
15 to 30 minutes keeping curing temperature
quenching in oil/hot bath/air 180 bis 220 °C
obtainable hardness: 53 HRC

Tempering:
slow heating to tempering temperature immediately after hardening; minimum time in furnace: 1 hour per 20 mm part thickness; tempering twice is recommended

Annealing graph: