Contacto

Estaremos encantados de atenderle de lunes a viernes desde las 8:00 hasta las 17:00. Haga clic en este enlace para buscar el interlocutor que le corresponde por zona.

Sede de Wolfurt
+43 5574 6706-0

Sus contactos

TIENDA

Carrito de la compra {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Artículo Cambiar carrito

Observaciones

Imagen

Artículo

Unidades

Precio por unidad

Precio total

Precio total con descuento

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Inicie sesión para ver los precios que se le aplican y continuar con el pedido.

Nuestra selecta gama facilita el material adecuado para cualquier aplicación.

M V10 PM Powder metallurgical steel

Designation

AISI:

A11 (PM)

Indicatory analysis:

C	2.45
Si	0.90
Mn	0.50
Cr	5.20
Mo	1.30
V	9.75

Strength:

max. 280 HB
(≈ max. 960 N/mm²)

Thermal conductivity at 100 °C:

20 W/m K

Character:

Powder metallurgical high-speed steel with optimal dimensional accuracy after the heat treatment, highest abrasive wear resistance and excellent toughness, good machinability through a homogeneous microstructure

Application:

Blocks for eroding, dies and cutting punches with extreme requirements,
fine blanking punches, pressing punches for sinter press tools

Treatment by

highly suitable:
Polishing, nitriding, EDM, coating

Heat treatment:

Soft annealing:
880 to 900 °C, about 2 to 5 hours
slow controlled cooling of 10 to 20 °C per hour
to about 600 °C; further cooling in air, max. 280 HB

Hardening:
Curing temperature: see tempering chart
quenching in oil/compressed gas/air/hot bath
obtainable hardness: 60-63 HRC

Tempering:
slow heating to tempering temperature (to avoid forming of cracks)
immediately after hardening;
triple tempering is recommended

Tempering chart:

TechnicalTip

Due to the high vanadium content the steel is enriched with small, hard carbides. This guarantees optimum edge stability with maximum abrasive wear resistance.
Ideally suitable for highly stressed parts
with complicated geometries.

To the mould making overview To the die making overview