Kontakt

Za Vas smo dostupni od ponedeljka do petka od 8:00 do 17:00 časova. Preko ovog linka možete pronaći kontakt osobe za Vaš region.

Sedište u Wolfurtu
+43 5574 6706-0

Vaše kontakt osobe

SHOP

Korpa {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Artikal Izmena pregleda korpe

Primedba

Slika

Artikal

kom.

Cena za jedan komad

Ukupna cena

Ukupna cena uklj. popust

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

: Prijavite se da biste videli svoje cene i nastavili da naručujete.

In our selected range you can find the right material for virtually any application.

1.3344 Powder metallurgical steel

Designation

DIN:	PM 6-5-3
AFNOR:	X 130 WMoCrV 6-5-4-3
UNI:	W 6 Mo 5 Cr 4 V 3
AISI:	M 3-2 (PM)

Chemical composition:

C	1.25
Si	0.30
Mn	0.30
Cr	4.00
Mo	5.00
V	3.00
W	6.20

Strength:

max. 265 HB
(≈ max. 905 N/mm²)

Thermal conductivity at 100 °C:

24 W/m K

Character:

powder metallurgy high-speed steel with good machinability, high resistance to adhesive and abrasive wear, with optimal toughness due to the uniform and fine carbide structure, very good through hardenability and high dimensional stability

Application:

blocks for eroding, cutting punches and dies with particularly durable edges; inserts with highest wear resistance

Treatment by

highly suitable:
Mirror polishing, nitriding, EDM, coating

Heat treatment:

Soft annealing:
860 to 880 °C for about 2 to 5 hours
slow controlled cooling of 10 to 20 °C per hour to about 600 °C; further cooling in air, max. 260 HB

Hardening:

— 1180 °C
--- 1150 °C

-·-· 1100 °C

curing temperature: see tempering chart
quenching in oil/compressed gas/air/hot bath
obtainable hardness: 64−66 HRC

Tempering:
Slow heating to tempering temperature (in order to avoid formation of cracks) immediately after hardening;
tempering three times is recommended

Annealing graph: