Contact

We are gladly available for you from Monday to Friday from 8:00 to 17:00. Use this link to find the contact persons for your region.

Headquarters Wolfurt
+43 5574 6706-0

Your contacts

SHOP

Shopping cart {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Items Change shopping cart

Remark

Picture

Items

Pcs

Single price

Total price

Total price incl. discount

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Please log in to see the precalculated prices and continue with the ordering process.

In our selected range you can find the right material for virtually any application.

1.3344 Powder metallurgical steel

Designation

DIN:	PM 6-5-3
AFNOR:	X 130 WMoCrV 6-5-4-3
UNI:	W 6 Mo 5 Cr 4 V 3
AISI:	M 3-2 (PM)

Chemical composition:

C	1.25
Si	0.30
Mn	0.30
Cr	4.00
Mo	5.00
V	3.00
W	6.20

Strength:

max. 265 HB
(≈ max. 905 N/mm²)

Thermal conductivity at 100 °C:

24 W/m K

Character:

powder metallurgy high-speed steel with good machinability, high resistance to adhesive and abrasive wear, with optimal toughness due to the uniform and fine carbide structure, very good through hardenability and high dimensional stability

Application:

blocks for eroding, cutting punches and dies with particularly durable edges; inserts with highest wear resistance

Treatment by

highly suitable:
Mirror polishing, nitriding, EDM, coating

Heat treatment:

Soft annealing:
860 to 880 °C for about 2 to 5 hours
slow controlled cooling of 10 to 20 °C per hour to about 600 °C; further cooling in air, max. 260 HB

Hardening:

— 1180 °C
--- 1150 °C

-·-· 1100 °C

curing temperature: see tempering chart
quenching in oil/compressed gas/air/hot bath
obtainable hardness: 64−66 HRC

Tempering:
Slow heating to tempering temperature (in order to avoid formation of cracks) immediately after hardening;
tempering three times is recommended

Annealing graph: