Kontakt

Vi står til rådighed mandag til fredag fra kl. 8:00 til kl. 17:00. Via dette link kan du finde din kontaktperson for dit område.

Central Wolfurt
+43 5574 6706-0

Din kontaktperson

SHOP

Kurv {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Produkt Skift indkøbskurv

Bemærkning

Billede

Produkt

Stk.

Enkeltpris

Samlet pris

Samlet pris inkl. rabat

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Log ind for at se dine priser og fortsæt bestillingen.

Vores udvalgte sortiment tilbyder det passende materiale til næsten alle anvendelser.

1.2842 Steel for through hardening

Designation

DIN:	90 MnCrV 8
AFNOR:	90 MV 8
UNI:	90 MnVCr 8 KU
AISI:	≈ O2

Chemical composition:

C	0.90
Si	0.20
Mn	2.00
Cr	0.40
V	0.10

Strength:

max. 230 HB
(≈ max. 780 N/mm²)

Thermal conductivity at 100 °C:

33 W/m K

Character:

steel for through-hardening with good machinability and high wear resistance; low warping and high dimensional stability; with high toughness and through hardenability (uniform hardness for cross sections 40 mm)

Application:

cavity plates and inserts exposed to abrasive stress; cutting punches; wear plates, cutting dies and guiding plates; guiding rails

Treatment by

unusual:
Polishing, etching, nitriding » 1.2379

is possible:
EDM, hard chroming

Heat treatment:

Soft annealing:
680 to 720 °C for about 2 to 5 hours; slow controlled cooling of 10 to 20 °C per hour to about 600 °C; further cooling in air, max. 220 HB

Hardening:
790 to 820 °C
Quenching in oil/hot bath
Obtainable hardness: 63-65 HRC

Tempering:
slow heating (to avoid forming of cracks) to tempering temperature immediately after hardening; tempering twice with intermediate cooling down to 20 °C increases the steel's toughness

max. obtainable hardness after tempering: 58−60 HRC

Annealing graph: