Kontakt

Vi ger personlig service från måndag till fredag, från 8:00 till 17:00. Via den här länken hittar du kontaktpersonen för din region.

Huvudkontor Wolfurt
+43 5574 6706-0

Din kontaktperson

SHOP

Varukorg {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Artikel Ändra varukorg

Anmärkning

Bild

Artikel

Enhetspris

Totalpris

Totalt pris inklusive rabatt

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Logga in för att se dina priser och fortsätta med beställningen.

I vårt stora sortiment finns lämpligt material för nästan alla användningsfall.

1.7225 Steel for quenching and tempering

Designation

DIN:	42 CrMo 4
AFNOR:	42 CD 4
UNI:	42 CrMo 4
AISI:	4140

Chemical composition:

C	0.42
Si	0.25
Mn	0.75
S	<0.035
Cr	1.10
Mo	0.22

Strength:

max. 217 HB
(≈ max. 740 N/mm²)

Tensile strength:

heat treated max. 720 N/mm²

Thermal conductivity at 20 °C:

42.6 W/m K

Character:

alloyedsteel, suitable for quenching and tempering, steel with high resistance and high toughness;
universally usable in engineering

Application:

machine construction, base plates, axes, gear shafts, gear wheels

Treatment by

is possible:
Nitriding, EDM, coating

unusual:

Welding

Heat treatment:

Normalising:
840 to 880 °C afterwards cooling in air; some components need tempering afterwards

Soft annealing:
680 to 720 °C for about 2 to 5 hours; slow controlled cooling of 10 to 20 °C per hour to about 600 °C; further cooling in air. Maximum 217 HB

Quenching:
max. 1.600 N/mm²

Hardening:
820 - 880 °C
quenching in oil or water
oil hardening for thin and complex,
water hardening for large and simple components
obtainable hardness: 53-61 HRC

Tempering:
slow heating to tempering temperature (to avoid forming of cracks) immediately after hardening; at least 60 minutes cooling in air

Annealing graph: