Contact

We are gladly available for you from Monday to Friday from 8:00 to 17:00. Use this link to find the contact persons for your region.

Headquarters Wolfurt
+43 5574 6706-0

Your contacts

SHOP

Shopping cart {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Items Change shopping cart

Remark

Picture

Items

Pcs

Single price

Total price

Total price incl. discount

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Please log in to see the precalculated prices and continue with the ordering process.

In our selected range you can find the right material for virtually any application.

1.2085 Tool steel

Designation

DIN:	X 33 CrS 16
AFNOR:	Z 35 CD 17.S
UNI:	-
AISI:	≈ 422 + S

Chemical composition:

C	0.33
Si	0.30
Mn	0.80
Cr	16.00
S	0.06
Ni	0.30

Strength:

280 - 325 HB
(≈ 950 - 1100 N/mm²)

Thermal conductivity at 100 °C:

18 W/m K

Character:

corrosion resistant, pre-toughened tool steel with good machinability due to Sulphur additive

Application:

plates for corrosion resistant mould bases and die sets;
moulds for corrosive plastics; the expense for protection and care of mould tools is reduced thanks to increased corrosion resistance; not suitable for mould inserts

Treatment by

unusual:
Polishing, etching, EDM, nitriding, hard chroming

Heat treatment:

Usually no heat treatment is required

Soft annealing:
850 to 880 °C for about 2 to 5 hours
slow controlled cooling, further cooling in air, annealing hardness max. 240 HB

Hardening:
1000 to 1030 °C
keeping curing temperature for 30 minutes
quenching in oil is preferable
obtainable hardness: 48 HRC

Tempering:
slow heating to tempering temperature immediately after hardening;
minimum time in furnace: 2 hour per 20 mm part thickness;
tempering twice is recommended

Annealing graph: