Контакт

От понеделник до петък от 8:00 до 17:00 часа ние сме на Ваше разположение. На тази линк ще намерите лицата за контакт за вашия регион.

Централата Волфурт
+43 5574 6706-0

Вашето лице за контакти

Магазин

Кошница {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Артикула Смяна на кошницата

Забележка

Снимка

Артикула

Брой

Единична цена

Обща цена

Обща цена с намалението

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Влезте в регистрацията си, за да видите актуалните цени и да задвижите поръчката.

Вие се интересувата от нашата фирма и продуктите ни? Тогава сте на точното място.

Coatings increase the service life of cutting punches

07.07.2020, Die making

The abrasive and adhesive wear that occurs during the stamping process on the cutting punch is minimised by coatings. This leads to a significant increase in the service life of cutting punches and consequently also reduces machine downtimes. In addition, the retracting forces are reduced due to the lower coefficient of friction. Different coatings are used depending on the materials to be punched. We give you an overview of the common coatings with their respective properties and application areas.

Titanium nitride

TiN is considered the classic standard coating and is often used today. This coating is tried and trusted for cutting tools. TiN coated cutting punches are suitable for sheet metal with low and medium hardness.

TiN coated cutting punch

Aluminium chromium nitride

AlCrN is the most commonly used ‘all-round coating’ and covers the largest area of application. In terms of performance, the AlCrN coating is clearly superior to the TiN coating. In contrast to TiN, this coating is also recommended for sheet metal with high hardness.

AlCrN coated cutting punch

Diamond-like carbon

The DLC coating has been used in mould making applications for some time now to minimise wear on guide pillars, centring devices and ejectors. Due to the very low coefficient of friction, DLC coated cutting elements are used for punching non-ferrous materials such as aluminium, brass or copper, as these are prone to galling.

DLC coated cutting punch

Comparison of coatings

	TiN	AlCrN	DLC
Coating colour	golden yellow	grey	black grey
Brand	Balinit® A TOP	Balinit® ALCRONA PRO TOP	Balinit® TRITON
Coating process	PVD	PVD	PACVD
Coating hardness [HV]	≈ 2.300	≈ 3.200	≈ 2.500
Coefficient of friction	≈ 0,4	≈ 0,35	≈ 0,1-0,2
Coating thickness [µm]	≈ 1,3 / 3*	≈ 1,3 / 2,5*	≈ 2

* depending on cutting edge diameter

Application example

The following graph compares the service life of the different coated punches.

Application example of coated cutting punches

Cutting punch: 1.3343 HSS (approx. 64 HRC)
Workpiece: Steel sheet C22 (≈ 1.0577), Thickness: 1,25 mm
Process parameter: 520 strokes / minute, Penetration depth: 2 mm

Configurable cutting punches with coating

In Meusburger’s innovative cutting punches configurator, the cutting punches can be individually configured with the desired coating in addition to the cutting dimensions, special length etc. The CAD data is then immediately available for download.