Contato

Estamos sempre disponíveis de segunda a sexta-feira, das 8:00 às 17:00. Utilize esta ligação para encontrar as suas pessoas de contacto consoante a sua região.

Sede em Wolfurt
+43 5574 6706-0

Os seus contactos

LOJA

Carrinho de compras {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Artigos Mudar carrinhos de compras

Observação

Imagem

Artigos

Unid.

Preço individual

Preço total

Preço total, incl. desconto

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Por favor, inicie a sessão para ver os seus preços e para continuar com a encomenda.

Na nossa gama selecionada, pode encontrar o material adequado para praticamente qualquer aplicação.

1.2316 Tool steel

Designation

DIN:	X 38 CrMo 16
AFNOR:	Z 35 CD 17
UNI:	X 38 CrMo 16 KU
AISI:	≈ 422

Chemical composition:

C	0.36
Cr	16.00
Mo	1.20

Strength:

280 - 325 HB
(≈ 950 - 1100 N/mm²)

Thermal conductivity at 100 °C:

18 W/m K

Character:

corrosion resistant, high-alloy, polishable, pre-toughened tool steel

Application:

moulds for processing corrosive plastics

Treatment by

good suitability for:

Polishing
is possible:

Etching, EDM

Nitriding:
reduces the corrosion resistance

Heat treatment:

already pre-toughened; usually no heat treatment required

Soft annealing:
760 to 800 °C for about 4 to 5 hours; slow controlled cooling of 10 to 20 °C per hour to about 650 °C; further cooling in air, max. 230 HB

Hardening:
1030 to 1050 °C
15 to 30 minutes keeping curing temperature
quenching in water/oil
obtainable hardness: 49 HRC

Tempering:
Slow heating to tempering temperature immediately after hardening. Minimum time in furnace: 1 hour per 20 mm part thickness

Annealing graph: